Our main products include 1/2inch to 16 inch ERW PIPE/GI PIPE which has been produced according to BS1387/ASTM A53/EN10219/EN10255/EN10217 Standard

PRODUCT

ABOUT US

Service Capability

Certificates

Project

Tianjin Lefin Industrial Co.,Ltd.

Our main products include 1/2inch to 16 inch ERW PIPE/GI PIPE which has been produced according to BS1387/ASTM A53/EN10219/EN10255/EN10217 Standard

OEM&ODM

Has rich experience in steel pipe processing, can be customized according to customer requirements according to the drawing and sample processing, assist in the development of new products.

PRODUCTS CENTER

Maldives STEEL HOLLOW SECTIONS

Maldives HOT DIP GALVANIZED STEEL PIPE

Maldives ASTM A53 GR.A WELDED PIPE

ASTM A53 GR.A Welded Pipe Outside Diameter: 1/2inch - 16inch Wall Thickness: 1.5MM - 16MM LENGTH:5 - 12M,commonly uesd,5.8M,6M,12M Surface Treatment: Galvanizing, Black vanish, Carving, threading, Slightly oil painting, PVC clothes cover each bundle ect.

Category:

MaldivesERW PIPE

+86 22 58171905

Inquire

Product Description

ASTM A53 Grade A is a specification for carbon steel pipes used in structural and low-pressure applications. It is part of the ASTM A53 standard, which includes different grades designed for specific uses. Grade A is known for its balance of affordability and adequate strength for medium to low-pressure applications.

Chemical Composition

Carbon (C): Up to 0.25%
Manganese (Mn): Up to 0.95%
Phosphorus (P): Up to 0.05%
Sulfur (S): Up to 0.045%
Copper, Nickel, Chromium, Molybdenum, Vanadium (total): Up to 1.00%

Physical Properties

Tensile Strength: A minimum of 330 MPa
Yield Strength: A minimum of 205 MPa
Elongation: Typically around 28%

These properties ensure that Grade A pipes can withstand certain levels of stress without permanent deformation or failure.

Differentiator between Grade A and Grade B

Chemical Requirements
Composition,max,%
	Carbon	Manganese	Phosphorus Sulfur	Sulfur	Copper^A	Nickel^A	Chromium^A	Molybdenum^A	Vanadium^A
Grade A	0.25^B	0.95	0.05	0.045	0.4	0.4	0.4	0.15	0.08
Grade B	0.3^C	1.2	0.05	0.045	0.4	0.4	0.4	0.15	0.08

^A The total composition for these five elements shall not exceed 1.00%.

^B For each reduction of 0.01% below the specified carbon maximum,an increase of 0.06% manganese above the specified maximum will be pemitted up to a maximum of 1.35%.

^C For each reduction of 0.01% below the specified carbon maximum,an increase of 0.06% manganese above the specied maximum wil be pemitted up to amaximum of 1.65%.

Grade B's higher carbon and manganese content result in increased strength and durability, making it suitable for more demanding applications.

Tensile Requirements
	Grade A	Grade B
Tensile strength,min,psi [MPa]	48000 [330]	60000 [415]
Yield strength,min,psi [MPa]	30000 [205]	35000 [240]
Elongation in 2 in.or 50 mm	uaually up to 28%	uaually up to 22%

Grade B's higher tensile and yield strengths make it more suitable for high-pressure applications.

CLICK HERE➡ "What Is ASTM A53 Standard"

Applications

Plumbing and Water Supply Systems: For lower pressure needs.
Structural Applications: In non-critical structural support roles.
Mechanical Tubing: Depending on wall thickness and specific mechanical requirements.

Advantages

Cost-Effectiveness: Grade A is more economical compared to higher grades.
Adequate Strength: Offers sufficient strength for low to medium pressure applications.
Wide Availability: Being a standard grade, it is widely available in the market.

ASTM A53 Grade A is a carbon steel pipe specification designed for lower pressure and non-critical applications. Its chemical composition and physical properties make it a cost-effective choice for applications where high strength is not a primary concern.